Gd3+xAl2-x系合金的晶体结构和磁熵研究
The Study of structure and magnetic entropy in Gd3+xAl2-x
生利英1,徐来自2,黄焦宏2
点击:2745次 下载:0次
作者单位:1. 包头职业技术学院材料系,内蒙古 包头 014030;2.包头稀土研究院,内蒙古 包头 014010
中文关键字:Gd3+xAl2-x;居里温度;磁熵;结构
英文关键字:Gd3+xAl2-x; Cure temperature; magnetic entropy; structure
中文摘要:采用真空高频磁悬浮炉制备出一系列的Gd3+xAl2-x(x=0,0.1,0.2,0.3)合金。通过Gd对Al的部分替代,研究了Gd元素微量替代对Gd3Al2合金结构和磁熵的影响。实验结果表明,Gd3+xAl2-x系合金的结构与Gd3Al2相同;随着Gd含量的增加,Gd3+xAl2-x系合金的居里温度和磁熵发生了变化。说明Gd对Al的部分替代改变了Gd3Al2合金的磁热效应。
英文摘要:A series of Gd3+xAl2-x(x=0,0.1,0.2,0.3)alloys were prepared in a high-frequency floating furnace. The effect of minor substitution of Al by Gd on the structure and magnetic entropy of Gd3Al2 alloy was investigated. As a result , the structure of Gd3+xAl2-x alloys is the same of Gd3Al2 alloy ,the Cure temperature and magnetic entropy of Gd3+xAl2-x alloys change with increasing content for Gd . It was revealed that minor addition of Gd can change the magnetocaloric effects of Gd3Al2 alloy.