MoBCoCr金属陶瓷涂层的磨粒磨损性能研究
Abrasive Wear Properties of MoBCoCr Cermet Coating
陈枭,纪岗昌
点击:2414次 下载:0次
作者单位:九江学院
中文关键字:MoB/CoCr;金属陶瓷;磨粒磨损
英文关键字:MoB/CoCr; Cermet; Abrasive wear
中文摘要:在310S基体表面采用低压等离子喷涂(LPPS)技术制备MoB/CoCr金属陶瓷涂层。通过扫面电镜观察涂层的组织结构;测试了MoB/CoCr涂层的显微硬度和结合强度;用湿式橡胶轮磨粒磨损试验机测试涂层的磨损性能。结果显示:MoB/CoCr涂层组织为层状结构,涂层与310S基体之间、表面涂层与过渡涂层之间结合良好。MoB/CoCr涂层具有较高的硬度值和结合强度,且具有良好的抗磨粒磨损性能。
英文摘要:MoB/CoCr cermet coatings were deposited by low pressure plasma spraying (LPPS) on 310S steel. The microstructure of the MoB/CoCr coating was observed by SEM. The properties of microhardness and bond strength of the MoB/CoCr coating were tested. The abrasive wear properties were evaluated by MLS-225 wet sand rubber wheel tester. The results show that MoB/CoCr coatings are dense and have excellent combination with 310S steel substrate. MoB/CoCr coating has high hardness and excellent wear properties.