热处理工艺对高铬白口铸铁滑动磨损的影响
Effect of Heat Treatment Process on Sliding Wear of High Chromium White Cast Iron
艾云龙,丁家圆, 何 文, 陈卫华
点击:3610次 下载:0次
作者单位:(南昌航空大学 材料学院,江西 南昌330063)
中文关键字:高铬白口铸铁; 滑动磨损; 热处理
英文关键字:high chromium white cast iron; sliding wear; heat treatment
中文摘要:分析了高铬白口铸铁的滑动磨损机制,研究了不同热处理工艺对材料的抗磨损性能的影响。实验结果表明,高铬白口铸铁的滑动磨损机制为粘着磨损和磨粒磨损的复合形式;在进行脱稳处理时,适度延长保温时间,使二次析出的碳化物团聚长大,有助于材料耐磨性能的提高。
英文摘要:The sliding wear mechanism between high chromium white cast iron and metal was analyzed, the effect of heat treatment processes on wear resistance was researched. The results show that the sliding wear mechanism are adhesive wear and abrasive wear, and during the quenching treatment, prolonging holding time can make the secondary carbides reunite and grow up, and improve wear resistance of the material.